Technical Data
N38SH Technical Specifications
| Parameter | Value |
|---|---|
| Remanence (Br) at 20°C | 12.2–12.6 kGs (1.22–1.26 T) |
| Coercive Force (HcB) at 20°C | ≥11.4 kOe (≥907 kA/m) |
| Intrinsic Coercivity (HcJ) at 20°C | ≥20 kOe (≥1592 kA/m) |
| Energy Product (BHmax) at 20°C | 36–39 MGOe (287–310 kJ/m³) |
| Nominal temperature class | 150°C |
| Approximate coefficient (Br) | -0.12 %/°C |
| Approximate coefficient (HcJ) | -0.50 %/°C |
| Density (typical) | 7.5 g/cm³ |
| Vickers Hardness (typical) | 550–650 HV |
Br, HcB, HcJ and BHmax are educational reference values at 20°C. Supplier specifications vary; agree the quoted material and acceptance limits separately. Temperature coefficients are approximate reference values, not a substitute for measured hot curves. Agree any batch measurements and certificate contents in the order specification.
Overview
What Is N38SH?
N38SH is a sintered NdFeB grade in the Super High Temperature (SH) family. This reference lists 12.2–12.6 kGs (1.22–1.26 T) remanence and ≥20 kOe (≥1592 kA/m) intrinsic coercivity at 20°C. The numeric grade describes energy product; the SH designation does not identify alloy composition or establish a safe operating point.
Applications
Related application design topics
These briefs describe design inputs and qualification questions. They do not confirm this grade for a particular application or geometry.
Surface Protection
Coating candidates for N38SH
Coating choice is driven by operating environment and assembly method. Qualify the finished coating stack for the actual part:
See our NdFeB Coatings Guide for coating definitions and qualification considerations.
Specifying
Design Considerations When Specifying N38SH
Key insight
The 150°C class is a preliminary screening value. Check the actual material's hot demagnetization curves against the load line, opposing field and duty cycle.
FAQ
Frequently Asked Questions
What is N38SH NdFeB magnet?
+
N38SH is a sintered NdFeB grade in the Super High Temperature (SH) family. This reference lists 12.2–12.6 kGs (1.22–1.26 T) remanence and ≥20 kOe (≥1592 kA/m) intrinsic coercivity at 20°C. The numeric grade describes energy product; the SH designation does not identify alloy composition or establish a safe operating point.
What is the maximum operating temperature of N38SH?
+
N38SH has a nominal 150°C class in this reference. Nominal temperature classes do not establish a safe operating temperature. Geometry, hot curves, load line, opposing field and duty cycle must be assessed for the actual part.
What is the BHmax of N38SH?
+
N38SH has a reference BHmax range of 36–39 MGOe (287–310 kJ/m³) at 20°C. BHmax is the maximum B × H product on the normal demagnetization curve. It does not specify hot output, surface field or pull force. Supplier acceptance values require a material-specific sheet or test record.
What applications use N38SH magnets?
+
Related design topics include EV Motors, Industrial Automation. These links are educational examples. Grade suitability requires the actual geometry, hot curves, load line, opposing field and duty cycle; the reference properties alone cannot establish it.
Request a drawing review for N38SH
Mainrich’s company range is N30 to N56. Grade, series, geometry and temperature must be confirmed together. Share your drawing, quantity and operating conditions for review.